Xitoyda yuqori sifatli AISI 310S ostenitik zanglamaydigan po'lat
Mar 18, 2026
Xabar QOLDIRISH
Kimyoviy tarkibi
| Element | Tarkibi (%) |
|---|---|
| Uglerod (C) | ≤ 0,08 |
| Marganets (Mn) | ≤ 2.00 |
| Kremniy (Si) | ≤ 1,50 |
| Fosfor (P) | ≤ 0,045 |
| Oltingugurt (S) | ≤ 0,030 |
| Chromium (Cr) | 24.0 - 26.0 |
| Nikel (Ni) | 19.0 - 22.0 |
| Azot (N) | ≤ 0,10 |
| Temir (Fe) | Balans |
⚙️ Mexanik xususiyatlari
| Mulk | Qiymat |
|---|---|
| Kuchlanish kuchi (xona harorati) | ≥ 515 MPa |
| Hosildorlik (0,2% ofset) | ≥ 205 MPa |
| Cho'zilish (50 mm o'lchagich) | ≥ 40% |
| Qattiqlik (Brinell) | ≤ 217 HB |
| Qattiqlik (Rockwell B) | ≤ 95 HRB |
| Ta'sir energiyasi (Charpy V-cho'qqisi) | ≥ 120 J |
| Young moduli | 200 GPa |
| Charchoq chegarasi (107tsikllar) | 240 MPa |
🔬 Jismoniy xususiyatlar
| Mulk | Qiymat |
|---|---|
| Zichlik | 7,98 g/sm³ |
| Erish nuqtasi | 1400-1450 ° S |
| Issiqlik o'tkazuvchanligi (20 ° C) | 14,2 Vt/m·K |
| Issiqlik kengayish koeffitsienti (20-100 ° C) | 14,4×10-6/K |
| Issiqlik kengayish koeffitsienti (20-1000 ° S) | 18,0×10-6/K |
| Maxsus issiqlik sig'imi | 500 J/kg·K |
| Elektr qarshiligi (20°C) | 0,78 mk·m |
| Magnit o'tkazuvchanlik | 1,02 µH/m (magnitsiz-) |
| Puasson nisbati | 0.27-0.30 |