Gnee po'latidan yuqori sifatli AISI 2205 dupleks zanglamaydigan po'lat
Mar 23, 2026
Xabar QOLDIRISH
🧪 Kimyoviy tarkibi
| Element | Tarkibi (%) |
|---|---|
| Uglerod (C) | 0,030 dan kam yoki unga teng |
| Marganets (Mn) | 2.00 dan kam yoki unga teng |
| Kremniy (Si) | 1,00 dan kam yoki unga teng |
| Fosfor (P) | 0,030 dan kam yoki unga teng |
| Oltingugurt (S) | 0,020 dan kam yoki unga teng |
| Chromium (Cr) | 22.0 - 23.0 |
| Nikel (Ni) | 4.5 - 6.5 |
| Molibden (Mo) | 3.0 - 3.5 |
| Azot (N) | 0.14 - 0.20 |
| Temir (Fe) | Balans |
⚙️ Mexanik xususiyatlari
| Mulk | Qiymat |
|---|---|
| Kuchlanish kuchi (Rm) | 620 - 880 MPa |
| Hosildorlik (Rp0,2) | 450 MPa dan katta yoki unga teng |
| Uzayish (A5) | 25% dan katta yoki teng |
| Qattiqlik (HRC) | 31 dan kichik yoki teng |
| Ta'sir energiyasi (KV 20 daraja) | 60 J dan katta yoki unga teng |
| Charchoq chegarasi (107tsikllar) | 280 MPa |
| Elastiklik moduli | 200 GPa |
| Puasson nisbati | 0.28 |
🔬 Jismoniy xususiyatlar
| Mulk | Qiymat |
|---|---|
| Zichlik | 7,8 g/sm³ |
| Erish nuqtasi | 1350 - 1400 daraja |
| Issiqlik o'tkazuvchanligi (20 daraja) | 14 W/m·K |
| Termal kengayish (20-100 daraja) | 13×10-6/K |
| Maxsus issiqlik sig'imi | 480 J/kg·K |
| Elektr qarshiligi (20 daraja) | 0.85 µΩ·m |
| Magnit o'tkazuvchanlik | Ferromagnit |
| Kyuri harorati | Taxminan 50 daraja |
📏 Mahsulot xususiyatlari
| Spetsifikatsiya | Mavjud variantlar |
|---|---|
| Mahsulot shakllari | Plitalar, choyshablar, barlar, novdalar, quvurlar, quvurlar, zarblar |
| Plitalar qalinligi | 3 - 150 mm |
| Plitalar qalinligi | 0.5 - 6 mm |
| Bar diametri | 6 - 300 mm |
| Quvurning tashqi diametri | 6 - 610 mm |
| Standartlar | ASTM A240, A479, A790, EN 10088-2, JIS G4305 |
| Yuzaki tugatish | 2B, BA, No.4, HL, Mirror, Tuzlangan |
| Tolerantlik | ±0,1 mm (qalinligi), ±1 mm (kenglik/uzunlik) |
| Uzunlik | 12 metrgacha (standart), moslashtirilgan uzunliklar mavjud |
So'rov yuborish