304 zanglamaydigan po'latdan zangga chidamlimi?
Feb 25, 2026
Xabar QOLDIRISH
Zanglamaydigan po'latdan kimyoviy tarkibi 304
1-jadval.304 zanglamaydigan po'latdan yasalgan qotishmalar uchun kimyoviy tarkibi
|
% |
304 |
304L |
304H |
|
C |
0.0 - 0.07 |
0.0 - 0.03 |
0.04 - 0.08 |
|
Mn |
0.0 - 2.0 |
0.0 - 2.00 |
0.0 - 2.0 |
|
Si |
0.0 - 1.00 |
0.0 - 1.00 |
0.0 - 1.0 |
|
P |
0.0 - 0.05 |
0.0 - 0.05 |
0.0 - 0.04 |
|
S |
0.0 - 0.03 |
0.0 - 0.02 |
0.0 - 0.02 |
|
Cr |
17.50 - 19.50 |
17.50 - 19.50 |
17.00 - 19.00 |
|
Ni |
8.00 - 10.50 |
8.00 - 10.50 |
8.00 - 11.00 |
|
Fe |
Balans |
Balans |
Balans |
|
N |
0.0-0.11 |
0.0-0.11 |
0.0 - 0.10 |
304 zanglamaydigan po'latning xususiyatlari
Zanglamaydigan po'latning mexanik xususiyatlari 304
Jadval 2a.Qalinligi 8 mm gacha bo'lgan 304 zanglamaydigan po'latdan yasalgan - varaq uchun mexanik xususiyatlar
|
Baho |
304 |
304L |
304H |
|
Kuchlanish kuchi (MPa) |
540 - 750 |
520 - 700 |
- |
|
Ishonchli stress (MPa) |
230 min |
220 min |
- |
|
Cho'zilish A50 mm |
45 min % |
45 min % |
- |
Jadval 2b.Qalinligi 8 - 75 mm dan 304 zanglamaydigan po'latdan yasalgan - plastinka uchun mexanik xususiyatlar
|
Baho |
304 |
304L |
304H |
|
Kuchlanish kuchi (MPa) |
520 - 720 |
500 - 700 |
- |
|
Ishonchli stress (MPa) |
210 min |
200 min |
- |
|
Uzayish A5 |
45 min % |
45 min % |
- |
Jadval 2c.304 zanglamaydigan po'latdan yasalgan qotishmalar uchun mexanik xususiyatlar - bar va diametri 160 mm gacha / qalinligi
|
Baho |
304 |
304L |
304H |
|
Kuchlanish kuchi (MPa) |
500 - 700 |
500 - 700 |
500 - 700 |
|
Ishonchli stress (MPa) |
190 |
175 min |
185 min |
|
Cho'zilish A50 mm |
45 min % |
45 min % |
40 min % |
|
Brinellning qattiqligi |
215 maksimal HB |
215 maksimal HB |
- |