Zanglamaydigan po'latning kimyoviy tarkibi 316
1-jadval.316 zanglamaydigan po'latdan yasalgan qotishmalar uchun odatiy kimyoviy tarkib
|
% |
316 |
316L |
316H |
316Ti |
|
C |
0.0-0.07 |
0.0-0.03 |
0.04-0.08 |
0.0- 0.08 |
|
Mn |
0.0-2.0 |
0-2.0 |
0.0-2.00 |
0.0-2.00 |
|
Si |
0.0-1.0 |
0.0-1.00 |
0.0-1.00 |
0.0- 1.00 |
|
P |
0.0-0.05 |
0.0-0.05 |
0-0.04 |
0.0-0.05 |
|
S |
0.0-0.02 |
0.0-0.02 |
0.0-0.02 |
0.0-0.03 |
|
Cr |
16.50-18.50 |
16.50-18.50 |
16.50-18.50 |
16.50- 18.50 |
|
Mo |
2.00-2.50 |
2.00-2.50 |
2.00-2.50 |
2.00- 2.50 |
|
Ni |
10.00-13.00 |
10.00-13.00 |
10.00-13.00 |
10.50- 14.00 |
|
Ti |
- |
- |
- |
0.40- 0.70 |
|
Fe |
muvozanat |
muvozanat |
muvozanat |
muvozanat |
316 zanglamaydigan po'latning xususiyatlari
Zanglamaydigan po'latning mexanik xususiyatlari 316
2-jadval.316 zanglamaydigan po'latdan yasalgan qotishmalar uchun odatiy mexanik xususiyatlar
|
Baho |
316 bar va bo'lim (qalinligi 160 mm gacha) |
316 varaq (qalinligi 8 mm gacha) | 316 plastinka (qalinligi 8 - 75 mm) | 316L Bar va qism (160 mm gacha) |
316L varaq (qalinligi 8 mm gacha) |
316 L Plitalar (qalinligi 8 - 75 mm) |
316H bar (160 mm gacha) |
316Ti bar(160 mm gacha) |
|
Kuchlanish kuchi (MPa) |
500 - 700 |
530 - 680 | 520 - 670 |
500 - 700 |
530 - 680 |
520 - 670 |
490 - 690 |
500 - 700 |
|
Ishonchli stress (MPa) |
200 min |
240 min | 220 min |
200 min |
240 min |
220 min |
205 min |
200 min |
|
Cho'zilish A50 mm |
40 min % |
40 min % |
45 min % |
40 min % |
40 min % |
45 min % |
35 % |
40 min % |
|
Brinellning qattiqligi |
215 maksimal HB |
- |
- |
215 maksimal HB |
- |
- |
- |
215 maksimal HB |