201 zanglamaydigan po'latdan yasalgan varaq
Mar 10, 2026
Xabar QOLDIRISH
| Standart |
ASTM A240, EN 10088-2, GB/T 3280 |
|---|---|
| Baho |
1.4372, SUS201, X12CrMnNiN17-7-5, Z12CMN17-07Az |
| Uzunlik |
2000 mm-6000 mm (78,74-236,22 dyuym), moslashtirilgan |
| To'liq kenglik |
1000 mm-2000 mm (39,37-78,74 dyuym), moslashtirilgan |
| Qalinligi |
0,3 mm-6 mm (0,012-0,24 dyuym), moslashtirilgan |
| Yuzaki tugatish |
2B, 8K, BA va boshqalar, HL, No1, No4 |
| Texnika |
Sovuq tortilgan, sovuq haddelenmiş, issiq haddelenmiş |
| Shakl |
Bobin, sovuq haddelenmiş choyshab, bo'rttirma choyshab va boshqalar, yassi plastinka va choyshab, issiq prokat, teshilgan choyshab, plastinka, sayqallangan choyshab, tasma, teksturali choyshablar |
Kimyoviy birikmalar
| Element | Uglerod (C) | Marganets (Mn) | Kremniy (Si) | Fosfor (P) | Oltingugurt (S) | Krom (Cr) | Nikel (Ni) | Azot (N) |
|---|
| Tarkibi (%) | 0,15 maks | 5.5-7.5 | 1,0 maks | 0,06 maksimal | 0,03 maksimal | 16.0-18.0 | 3.5-5.5 | 0,25 maks |
Mexanik xususiyatlar
| Xususiyatlari | Metrik birlik | Imperator birligi |
|---|
| Mustahkamlik chegarasi | 655 – 860 MPa | 95 - 125 ksi |
| Hosildorlik kuchi | 450 MPa | 65 ksi |
| Vickers qattiqligi | 230 - 270 HV | 230 - 270 HV |
| Brinell qattiqligi | 200 - 250 HB | 200 - 250 HB |
| Rokvellning qattiqligi | 50 - 56 HRC | 50 - 56 HRC |
| Cho'zilish | 20% | 20% |
| Elastik modul | 200 GPa | 29 x 10^6 psi |
Keyingi2: 1.4550 zanglamaydigan po'lat nima?